NGAC P907-01
High Temperature Fiber Optic Epoxy Adhesive
GR-326 CERTIFIED
To request a FREE sample of NGAC P907-01, complete the form or email us directly at info@nextgenadhesives.com.
DESCRIPTION:
NGAC P907-01 is a rapid curing, low viscosity, heat cured epoxy adhesive system that is specifically formulated for use in the fiber optic industry.
ADVANTAGES AND APPLICATIONS:
Uses include bonding fiber optic bundles, potting glass fiber bundles and termination of single mode and multimode fiber optic connectors. NGAC P907-01 is a low viscosity mixture that ensures exceptional wicking and wetting of the fibers, along with superior adhesion strength.
NGAC P907-01 features the following characteristics that enable ease of use.
STORAGE REQUIREMENTS:
NGAC P907-01 packaged in XPAKs should be stored at 12- 25°C, if crystallization of the resin occurs, place XPAK with pin in place in a 65°C oven for 15 minutes, allow to cool and proceed per normal procedures. NGAC P907-01 packaged in PM&F syringes should be stored at -40°C.
PROPERTIES:
*All values reported below are typical values and are for reference use only. These values are not intended for use in developing specifications. Application testing under specific conditions should be performed to determine actual results and fitness for use.
COLOR:
Resin - Amber
Hardener - Amber
Mixed, After Cure - Amber/Brown
SPECIFIC GRAVITY: 1.20
VISCOSITY: 2,500 cps
REFRACTIVE INDEX: 1.56
MIX RATIO BY WEIGHT (R/H): 100/10
HARDNESS, Shore D: >85
OPERATING TEMPERATURE: -60 to +250˚C
GLASS TRANSITION (Tg), Ultimate: 120°C
PERCENT SOLIDS: 100%
WORKING LIFE: 4 hours
CURE SCHEDULE:
Temperature of 100˚C for 5 minutes
OR
Temperature of 120˚C for 2 minutes
OR
Temperature of 150°C for 1 minute
*For maximum physical properties a post-cure for 15 minutes at 120°C is recommended
For additional information or assistance, please call 978-436-9600.